F7A2 EM12K Submerged ARC Welding flux for LPG Cylinder body

HIGENERAL NEW MATERIALS CO.,LTD

F7A2 EM12K Submerged ARC Welding flux for LPG Cylinder body

  • 1
  • 2
  • 3

Brand Name : HGSJ

Model Number : F7A2-EM12K

Certification : ISO9001

Place of Origin : China

MOQ : 10 MTS

Price : USD430/MT

Payment Terms : T/T

Supply Ability : 3000/MONTH

Packaging Details : POLY PLATIC PAPER BAG

welding : submerged arc welding

welding flux : submerged are welding

agglomerated : agglomerated flux

Contact Now

SUBMERGED ARC WELDING FLUX

Name of products: Agglomerated flux SJ302

Silicon- Calcium Agglomerated flux

Execute standards: GB/T 5293-1999 GB F5A2-H08MnA;

( Equivalent to AWS F7A2 -EM12K; AWS F7A0 – EL12; )

Description of flux :

Agglomerated flux SJ302 is a kind of agglomerated flux type Silicon and Calcium with ball form granular of brown, Bllw≈1.1;about 10 – 60 mesh in size. It is suitable for AC or DC(+) power. It has stable ARC, neat bead appearance and shows good weld-ability. The slag detachability is better than that of SJ301. it is suitable for the girth welding of different diameter. This flux has good anti-humidity absorption. The anti-cracking property is better than other flux with good impact toughness.

Application of Welding Flux:

In combination with wire EL8, EM12K, EA1 and etc. this flux is suitable for the welding of structures, boilers, pipelines and etc.

Typical Flux Composition Range: ( %)

SIO2+ TIO2 CaO + MgO MNO+AL2O3 CAF2 OTHERS
20—25 % 20 + 25% 30—40% 8 -- 10% ---

Typical Mechanical Properties Of :

( GB/T5293-1999 F5A2-H08MnA WELDING WIRE ) Impact testing

TEST ITEM

tensile strength

(σb)(Mpa)

yield strength

σs (MPa)

Elongation

(δ5)%

AKV (J) -30℃

Centigrade

Guarantee value 480 – 650 ≥ 400 ≥ 24 ≥ 34
Tested value 590 460 32 100 / 90 / 130

Guideline for usage:

1.--- Dry the flux at 300℃ – 350℃ for 2 hours before use.

2. ---Completely remove Rust, Oil and Dirt from the groove surface prior to welding.

NOTE:

Agglomerated flux use a binding agent to hold materials together, are baked, and broken up. Agglomerated fluxes are easier to customize for an application, and can provide various alloying elements needed for welding.


Quality F7A2 EM12K Submerged ARC Welding flux for LPG Cylinder body for sale

F7A2 EM12K Submerged ARC Welding flux for LPG Cylinder body Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: HIGENERAL NEW MATERIALS CO.,LTD
*Subject:
*Message:
Characters Remaining: (0/3000)